W85 tungsten copper plate is composed of 85% W and 15% Cu, its density reaches(15.90g/cm3), hardness more than HB240, electric conductivity is 38%IACS, softening temperature is ≥900℃, thermal conductivity coefficient is between 180-200 (wm/k) and the coefficient of expansion is 7.0-7.5 (10-6k).

W80 tungsten copper plate is composed of 80% W and 20% Cu so that high hardness and melting point characteristics of tungsten is more obvious. Its density is up to 15.15g/cm3, hardness reaches more than HB140, but due to less Cu, conductivity is decreasing to 34%IACS, softening temperature is ≥900℃,the bending strength is 980, the thermal conductivity is 190-210(wm/k) and the coefficient of expansion is 8.0-8.5(10-6K).

W75 tungsten copper plate is composed of 75% W and 25% Cu, which not only has high density (14.50g/cm3), high hardness (≥HB195), high strength, but also has good conductivity (%38IACS), softening temperature is ≥900℃, thermal conductivity coefficient is between 200-230 (wm/k) and the coefficient of expansion is 9.0-9.5 (10-6k).

W70 tungsten copper plate is composed of 70% W and 30% Cu so that it is harder than W50 and W60 rods. Its density is up to 12.75g/cm3, hardness reaches more than HB140, and conductivity is 47%IACS, softening temperature is ≥900℃ and the bending strength is 790.

W65 tungsten copper plate has many advantages, such as excellent electrical and thermal conductivity, uniform texture, high density, high-temperature resistance and arc erosion resistance, which can be widely used in high-temperature materials, high-voltage switch with electrical alloy, EDM electrodes, and microelectronic materials.

W60 tungsten copper plate is composed of 60% W and 40% Cu, which not only has high density (12.75g/cm3), high hardness (≥HB140), high strength, but also has good conductivity (%47IACS), softening temperature is ≥900℃.

W50 tungsten copper plate is composed of 55% W and 45% Cu, which not only has high density (11.85g/cm3), high hardness (≥HB115), high strength, but also has good conductivity (%54IACS), softening temperature is ≥900℃.

W50 tungsten copper plate is composed of 50% W and 50% Cu, which not only has high density (11.85g/cm3), high hardness (≥HB115), high strength, but also has good conductivity (%54IACS), softening temperature is ≥900℃.

Ø14x200mm tungsten copper rod with diameter of Ø14mm and length of 200mm, the general diameter tolerance is ±0.5mm and length tolerance is 0 to +5mm. It can be applied to heavy-duty sliding friction, high-speed and moving solid seals. Various instruments require non-magnetic, low expansion, high elastic modulus, shielding and other special requirements.

Ø12x200mm tungsten copper rod with diameter of Ø12mm and length of 200mm, the general diameter tolerance is ±0.5mm and length tolerance is 0 to +5mm. High-density Ø12x200mm tungsten copper rods used as high-temperature components such as gas rudders, nozzles, throat linings, and nose cones that are ablated and washed by high-temperature, high-speed airflow such as rockets and missiles.